Less odor, less VOCs, odor class 3.0
Long open time, good initial tack and bonding strength
Excellent temperature resistance, high-temperature resistant up to 90℃, low-temperature resistant up to -30℃
FIELDS OF APPLICATION
For auto interior decoration, mainly used for composite forming of carpet, luggage lid and trunk lid
|Main ingredients||Polyolefin resin|
|Softening point||130±10℃||GB/T 15332-1994|
|Peeling strength||≥70N/2.5cm||GB/T 2790-1995|
|Viscosity||4500±700 mPa·s(180℃)||HG/T 3660-1999|
Hot melt glue gun, spray, roller;
Service temperature 160~180℃(summer), 170~185℃(winter), increase 5℃ at nozzle, keep setting temperature of glue hose same with machine;
Suggest glue spread 70-80g/m2.
INSTRUCTIONS FOR USE
Suggest to use hot melt machine with temperature control function;
Service temperature shall not ≥185℃;
Better to choose MDF with water content at 6-12%, high water content will cause bubbles that influence the bonding strength. Go through drying treatment if water content is high, put MDF under room temperature if water content is low;
Suggested working humidity >RH50%.
Conveyable after composite, adjusting the delivery time according to the temperature and humidity of environment.
SHELF LIFE AND STORAGE CONDITIONS
Shall be stored in indoor, cool and dry place, avoid direct sunlight and constant high temperature
2 years (sealed)